Non-halogen Printable Polycarbonate Film Sheets
1.Widely used in Insulation Field,such as TV/monitor,electrical applicance,etc..
2.Flam-retardant grade
3.Factory supply
4.Be delivered in stock
Specification:
Grade
|
Color
|
Texture
|
Thickness(mm)
|
Widt(mm)
|
KLX PC-1860
|
Natural
|
velve/tMatte
|
0.05-1.000
(0.002″-0.040″)
|
610&930&1230
(2′&3′&4′)
|
KLX PC-1860-1
|
Natural
|
Polished/Polished
|
KLX PC-1860W
|
White
|
velve/tMatte
|
KLX PC-1860B
|
Black
|
velvet/Matte
|
KLX PC-1860-83B
|
Black
|
Polished/Matte
|
0.125-0.200
(0.005″-0.008″)
|
Application:
Offer ease of thermoforming, hydroforming, embossing, diecutting, folding and bending and are the excellent films for applications such as printed circuit board insulation, power supply insulation, displays insulation, TV/monitor insulation, electrical appliance insulation and shielding.
Thickness
(mm)
|
N. Weight per roll
(KG)
|
Pound
(LB)
|
Width × Length
(mm × m)
|
Width × Length
Foot × Foot
|
0.05(0.002")
|
55
|
121
|
610×1503
|
2′ ×4931′
|
0.075 (0.003")
|
60
|
132
|
610×1093
|
2′ ×3586′
|
0.1 (0.004")
|
78
|
172
|
930×699
|
3′ ×2293′
|
0.125 (0.005")
|
89.3
|
197
|
930×640
|
3′×2067′
|
0.175 (0.007")
|
89.3
|
197
|
930×457
|
3′×1498′
|
0.25 (0.010")
|
89.3
|
197
|
930×320
|
3′×1049′
|
0.38 (0.015")
|
89.3
|
197
|
930×210
|
3′×688′
|
0.43(0.017")
|
89.3
|
197
|
930×186
|
3′×610′
|
0.50 (0.020")
|
89.3
|
197
|
930×160
|
3′×524′
|
0.76 (0.030")
|
89.3
|
197
|
930×105
|
3′×344′
|
1.0 (0.040")
|
89.3
|
197
|
930×80
|
3′×262′
|
Sheets Packing Details
Size
|
N. Weight per Sheet
|
Pcs/pack
|
Pcs/pallet
|
KG
|
LB
|
0.50mm× 930mm× 1830mm(0.020″×3′×6′)
|
1.02
|
2.25
|
20
|
600
|
0.70mm× 930mm× 1830mm(0.028″×3′×6′)
|
1.43
|
3.15
|
20
|
400
|
0.76mm× 930mm× 1830mm(0.030″×3′×6′)
|
1.55
|
3.42
|
20
|
400
|
0.80mm× 930mm× 1830mm(0.032″×3′×6′)
|
1.63
|
3.59
|
20
|
400
|
1.0mm× 930mm× 1830mm (0.040″×3′×6′)
|
2.04
|
4.50
|
10
|
300
|
Typical Property Values
Property
|
Item
|
Test Method
|
Unit
|
Standard Value
|
Physical
Performance
|
Density
|
ASTM D792
|
g∕cm3
|
1.2
|
Absorption Rate,24hrs
|
ASTM D570
|
﹪
|
<0.35
|
Haze
|
ASTM 1003
|
%
|
<1
|
Tensile Strength
|
ASTM D882
ISO527
|
psi
MPa
|
7500
52
|
Mechanical Performance
|
Tensile Elongation at Break
|
ASTM D882
|
﹪
|
100
|
Impact Strength(0.75mm)
|
ASTM D3029
ISO 6603-1
|
ft-lb
J
|
11
28
|
Tear Strength Propagation
|
ASTM D1922
|
g/mil
|
>30
|
Vicat Softening Temperature
|
ASTM D1525
|
℃
|
135
|
Thermal Performance
|
Shrinkage at 135℃
|
ASTM D1204
|
%
|
<1.0
|
Dielectric Strength(0.25mm)
|
ASTM D149
|
v/mil
|
1350
|
Electrical Performance
|
Surface Resistivity 25℃,50%RH
|
ASTM D257
|
Ω
|
>1.0×1015
|
Volume Resistivity 25℃,50%RH
|
ASTM D257
|
Ω·cm
|
>1.0×1016
|
UL Flammability
|
Film thickness <0.25 mm
|
UL BULLETIN 94
|
UL94
|
VTM-0
|
Film thickness ≥0.25 mm
|
V-0
|
Environment Protection Index
Index
|
Value
|
Mercury (Hg)
|
N.D(<2ppm)
|
Hexavalent Chromium Cr (VI)
|
N.D(<2ppm)
|
Cadmium (Cd)
|
N.D(<2ppm)
|
Lead (Pb)
|
N.D(<2ppm)
|
Sum of PBBs
|
N.D(<5ppm)
|
Sum of PBDEs
|
N.D(<5ppm)
|
Chlorine(Cl)
|
N.D(<5ppm)
|
Bromine(Br)
|
N.D(<5ppm)
|